17 4 Stainless Steel Condition H1025

As with other precipitation hardening alloys al 17 4 pre cipitation hardening alloy is more susceptible to stress.

17 4 stainless steel condition h1025.

Our h1025 has been heat treated to the minimum tensile strength of 155ksi yield strength of 145ksi an elongation in 2in of 12 and a reduction of area of 45. Cobalt is reported in the chemistry. Rockwell c 38 average condition h1150 1150 f for 4 hours air cool. Equivalent materials of 17 4 h1025 stainless steels.

17 4 stainless steel bar 17 4ph cres condition a round bar supplier tw metals. In din standard the equivalent material is referred as 1 4542 type steel. Al 17 4 precipitation hardening alloy is comparable to that of type 304 stainless steel in most media. Home resources product information stainless grades precipitation hardening grades 17 4ph h1025 17 4ph h1025 penn stainless inventory now includes alloy 17 4 h1025 uns s17400 in sheet sheet coil plate round bar processed flat bar and tubular products.

Condition h1025 1025 f for 4 hours air cool. Stainless steel 17 4 h1025 is a precipitation hardening martensitic stainless steel which has corrosion resistance comparable to austenitic varieties. The equivalent materials for 17 4 h1025 stainless steels specified in other recognized standards are listed as under. In european standard the equivalent material is referred as x5crnicunb16 4 type steel.

Sandmeyer steel company stocks a large inventory of 17 4ph stainless steel plate in the annealed condition in thicknesses from 3 16 through 3 ready to be processed and shipped to your specific requirements. Stainless steel 17 4 h1075 is stainless steel grade 17 4 also known as 630 alloy that has been heat treated at a temperature between 1065 f and 1085 f for 3 75 hours to 4 25 hours. 17 4 stainless generally conforms to astm a564 type 630 ams 5643. After treating the steel at a temperature of 1075 or higher it will become softer than in the annealed form.

Steel grades17 4ph chemical information mechanical properties physical properties mechanical properties heat treatment and micro structure temperat ure time brinell rockwell c a 1038 c 1 2 oil air to below 32 c 363 max. 17 4 is a chromium nickel copper precipitation hardening stainless steel used for applications requiring high strength. H900 480 c 1 air 420 44 h925 495 c 4 air 409 42 h1025 550 c 4 air 352 38 h1075 580 c 4 air 341 36.